Density 6.0g/Cm3 Yttrium Stabilized Zirconia Grinding Media 2.6-2.8mm
Product Description of Yttrium Stabilized Zirconia Grinding Media
Zirconia grinding beads, also known as ceramic milling beads, is made of ultra-fine, highly active zirconia powder by sintering process, with yttrium oxide as the stabilizer, with ZrO2 95%.
Zirconia beads are of multi sizes, ranging from 0.1mm to 50mm, with a high density of 6.0g/cm3. It has the characteristics of anti-aging, low wear and no pollution. It is widely used for dispersion of media and high viscosity pastes with different color requirements and different chemical conditions, such as lithium battery anode and cathode materials, magnetic materials, calcium carbonate, titanium dioxide, coatings, adhesives, pigments, dyes, paint, inks, etc.
Specification of Yttrium Stabilized Zirconia Grinding Media
Manufacturing process: Sintering Method
| Chemical composition | ZrO2 95% Min. Y2O3 4.5% Min |
| Color | Shiny white |
| Shape | Sphere/ Bead / Ball |
| Density | 6.0g/cm³ Min. |
| Specific density | 3.7g/cm³ Min. |
| Moh's hardness | 9 |
| Impact Strength | 2.9KN (2mm) |
| Compressive Strength | 5500MPa |
| Modulus of Elasticity | 200Gpa |
| Package | 25kg/barrel |
| SIZES Φ MM |
| 0.1-0.2 | 0.2-0.3 | 0.3-0.4 | 0.4-0.6 | 0.6-0.8 |
| 0.8-1.0 | 1.0-1.2 | 1.2-1.4 | 1.4-1.6 | 1.6-1.8 |
| 1.8-2.0 | 2.0-2.2 | 2.2-2.4 | 2.4-2.6 | 2.6-2.8 |
| 2.8-3.0 | 4,5,6,7,8,9,10,12,15,17,20,25,30,40,50 |
Features of Yttrium Stabilized Zirconia Grinding Media
1. Very low wear (ppm) to prevent material contamination
2. High grinding efficiency
3. Extremely long service life and low comprehensive use cost
4. Suitable for high viscosity, wet grinding and dispersion
Application of Yttrium Stabilized Zirconia Grinding Media
1. Wear and corrosion resistant products: coatings, textiles, pigments, printing and dyeing
2. High strength and high toughness products: magnetic materials, piezoelectric ceramics, dielectric ceramics
3. Prevention of pollution: medicine, food, cosmetics
4. Ceramics: electronic ceramics, refractory ceramics, structural ceramics
Applicable Equipment of Yttrium Stabilized Zirconia Grinding Media
Horizontal sand mill, turbine horizontal sand mill, vertical sand mill, centrifugal sand mill, basket sand mill, ball mill, etc
Rod Mixer, Disc Mixer, Screw Mixer, Impeller Mixer
Instructions in use:
1. According to the viscosity, hardness, dispersed particle size and grinding requirements of grinding materials, select the corresponding varieties, specifications and quantities of zirconium beads.
2. Clean the zirconium bead and the inner wall of the grinder barrel before grinding.
3. First, put the materials to be ground into the barrel of the grinder, and then put in an appropriate amount of zirconium beads. After the grinder runs, add zirconium beads gradually. The filling amount is generally 70% - 85% of the volume of the barrel of the grinder.
4. Do not allow the zirconium bead to run for a long time when the grinder is short of material. Otherwise, the grinder is easy to be damaged
5. After the grinding machine runs for a period of time, zirconium beads should be supplemented appropriately to ensure the grinding quality and efficiency.